EN 10305-one E235 C seamless steel vehicle and truck tube
Higher CZPT Seamless Steel Tube for Automotive Market and CZPT Software
Programs
one. Automotive fields
A. Gasoline injection traces/nozzles
B. CNG (Compressed Nature Gasoline) tube– Burst strain: 1307Bar, Doing work Pressure: close to 350bar
C. Push transmission: Steering column elements
D. Equipment shafts, hand brake, entrance axles, airbag inflators, stabilizers, seat fasteners, front-wheel travel shafts
E. Shock absorber and others
two. CZPT Fields
A. CZPT circuits (HPL), pneumatic strains, and hydraulic suspension technique
B. CZPT cylinders (HPZ)
three. Other Fields
CZPT equipment, CZPT cylinder, heat exchanger, high precision devices, oil lines, and other people in need
Additional Surface area Therapy Following TUBE MACZPT
one. Galvanizing
A. Silver galvanized
B. Yellow galvanized
C. CZPT green coated
Layer thickness: 8-20um, Salty Spray Test: 48-150 hours
2.Black phosphate
| Content Chemical Composition (%) | |||||||||
| Standard | Steel Grade | Material Number | C | Si | Mn | P | S | Cr | Mo |
| DIN 2391 | ST35 | 1.0308 | <= 0.17 | <= 0.35 | >=.04 | <=0.571 | <=0.571 | – | – |
| ST45 | one.0408 | <= 0.21 | <= 0.35 | >=.04 | <=0.571 | <=0.571 | – | – | |
| ST52 | 1.058 | <= 0.22 | <= 0.55 | <=1.60 | <=0.571 | <=0.571 | – | – | |
| BK | BKW | BKS | GBK | ||||||
| Steel Grade | Rm Tensile Strength (Mpa) Min | A Elongation(%) Min | Rm Tensile Toughness (Mpa) Min | A Elongation(%) Min | Rm Tensile Energy (Mpa) Min | Rel Produce Power(Mpa) Min | A Elongation (%) Min | Rm Tensile Energy (Mpa)Min | A Elongation (%)Min |
| ST35 | 480 | six | 420 | 10 | 420 | 315 | fourteen | 315 | twenty five |
| ST45 | 580 | 5 | 520 | eight | 520 | 375 | 12 | 390 | 21 |
| ST52 | 640 | 4 | 580 | seven | 580 | 420 | ten | 490 | 22 |
| Common | Steel Grade | Substance Quantity | C | Si | Mn | P | S | Cr | Mo |
| EN10305-1 EN10305-4 |
E235 | one.0308 | <= 0.17 | <= 0.35 | >=.04 | <=0.571 | <=0.571 | – | – |
| E255 | one.0408 | <= 0.21 | <= 0.35 | >=.04 | <=0.571 | <=0.571 | – | – | |
| E355 | one.058 | <= 0.22 | <= 0.55 | <=1.60 | <=0.571 | <=0.571 | – | – |
| Metal Grade | (+C) | (+LC) | (+SR) | (+A) | (+N) | |||||||
| Rm Tensile Strength (Mpa) Min | A Elongation(%) Min | Rm Tensile Energy (Mpa) Min | A Elongation(%) Min | Rm Tensile Energy (Mpa) Min | Rel Generate Strength(Mpa) Min | A Elongation (%) Min | Rm Tensile Power (Mpa)Min | A Elongation (%)Min | Rm Tensile Power (Mpa) | Rel Produce Strength (Mpa) Min | A Elongation (%) Min | |
| E235 | 480 | 6 | 420 | ten | 420 | 350 | sixteen | 315 | twenty five | 340-480 | 235 | 25 |
| E255 | 580 | 5 | 520 | eight | 520 | 375 | twelve | 390 | 21 | 440-570 | 255 | 21 |
| E355 | 640 | 4 | 580 | seven | 580 | 450 | 10 | 450 | 22 | 490-630 | 355 | 22 |
| Content Chemical Composition (%) | |||||||||
| Steel Grade | Materials Amount | C | Si | Mn | P | S | Cr | Mo | |
| GB/T 8162 GB/T 8163 GB/T 3639 |
ten | – | .07-.fourteen | .17-.35 | .35-.65 | <=0.035 | <=0.04 | – | – |
| twenty | – | .seventeen-.23 | .17-.37 | .35-.65 | ≤0.035 | ≤0.035 | – | – | |
| 45 | – | .forty two-.50 | .seventeen-.37 | .fifty-.eighty | ≤0.035 | ≤0.035 | – | – | |
| Q345B/16Mn | – | ≤0.20 | ≤0.fifty | <=1.70 | ≤0.035 | ≤0.035 | – | – | |
Many other steel grades and CZPT – modified steel grades are available on request
| Some samples of relevant metal quality | ||||||
| GB | TOCT | ASTM | BS | JIS | NF | DIN |
| 10F | 1571 | 040A10 | XC10 | |||
| 10 | 10 | ten,a hundred and one,012 | 045M10 | S10C | XC10 | C10,CK10 |
| 20 | twenty | 1571 | 050A20 | S20C | XC18 | C22,CK22 |
| forty five | 45 | 1045 | 080M46 | S45C | XC45 | C45,CK45 |
| 30CrMo | 30XM | 4130 | 1717COS110 | SCM420 | 30CD4 | |
| 42CrMo | 4140 | 708A42 | 42CD4 | 42CrMo4 | ||
| 708M40 | ||||||
| 35CrMo | 35XM | 4135 | 708A37 | SCM3 | 35CD4 | 34CrMo4 |
Delivery conditions: CZPT tubes are delivered in following conditions (first symbol lists previous designation, the new one according to EN is in brackets):
BK (+C) Cold finished/hard (cold finished as drawn).
No heat treatment after last cold forming process.
BKW (+LC) Cold finished/soft (lightly cold worked).
After last heat treatment there is a light finishing pass (cold drawing).
BKS (+SR) Cold finished/stress relieve annealed.
After the final cold forming process the tubes are stress relieve annealed.
GBK (+A) Annealed.
After the final cold forming process the tubes are annealed in a controlled atmosphere.
NBK (+N) Normalized.
After the final cold forming process the tubes are annealed above the upper transformation point in a controlled atmosphere.
Assessments: all tubes are checked according to the relevant production standardsupplementary/optional tests are available on request chemical mechanical and technological tests are made according to relevant standard
Certificates: according to EN 15714 3.1
Packed in bundles or bins